Unusual tensile and fracture behavior of pure copper at high levels of neutron-induced swelling

Keyphrases

• Ductility 100%
• Fracture Behavior 100%
• Neutron 100%
• Tensile Behavior 100%
• Pure Copper 100%
• Uniform Elongation 100%
• Irradiation 66%
• Area Reduction 66%
• Grain Boundary 33%
• Fracture Surface 33%
• Crack Propagation 33%
• Displacement per Atom 33%
• Fracture Mode 33%
• Behavior Change 33%
• Gliding 33%
• Serpentine 33%
• Significant Level 33%
• Fast Neutrons 33%
• Propagation Failure 33%
• Fracture Morphology 33%
• Sudden Failure 33%
• Unilateral Shift 33%
• Total Elongation 33%

Engineering

• Fracture Behavior 100%
• Tensile Loads 100%
• Pure Copper 100%
• Crack Propagation 50%
• Grain Boundary 50%
• Fracture Surface 50%
• Fast Neutron 50%
• Fracture Morphology 50%

Material Science

• Fracture Behavior 100%
• Tensile Loads 100%
• Grain Boundary 50%
• Crack Propagation 50%