TEM-induced structural evolution in amorphous Fe oxide nanoparticles

Andrew H. Latham, Mark J. Wilson, Peter Schiffer, Mary Elizabeth Williams

Research output: Contribution to journalArticlepeer-review


Exposure to the high energy electron beam of a TEM changes the morphology of amorphous Fe oxide nanoparticles from solid spheres to hollow shells. Amorphous Fe oxide nanoparticles prepared via high-temperature methods using hexadecylamine and trioctylphosphine oxide surfactants were compared to crystalline γ-Fe2O3 particles of similar size. Both sets of particles are fully characterized via SQUID magnetometry, X-ray powder diffraction, BET surface analysis, EPR spectroscopy, high-resolution transmission electron microscopy (TEM), and electron energy loss spectroscopy (EELS). Time-resolved TEM images reveal that the amorphous Fe oxide particles evolve from solid spheres into hollow shells in <2 min, whereas crystalline γ-Fe2O3 are unaffected by the electron beam. The resulting nanocrystalline Fe oxide shells bear striking resemblance to core-shell nanocrystals, but are a result of a morphology change attributed to restructuring of particle voids and defects induced by quasi-melting in the TEM. These results thus imply that caution is necessary when using TEM to analyze nanoparticle core-shell and heterostructured nanoparticles.

Original languageEnglish (US)
Pages (from-to)12632-12633
Number of pages2
JournalJournal of the American Chemical Society
Issue number39
StatePublished - Oct 4 2006
Externally publishedYes

ASJC Scopus subject areas

  • Catalysis
  • General Chemistry
  • Biochemistry
  • Colloid and Surface Chemistry


Dive into the research topics of 'TEM-induced structural evolution in amorphous Fe oxide nanoparticles'. Together they form a unique fingerprint.

Cite this