Precipitate induced anisotropy effects in aluminium alloys

T. Foglesong, H. Sehitoglu, H. J. Maeir

Research output: Contribution to journalConference articlepeer-review


A physically-based hardening formulation, derived from dislocation theory, was incorporated into a polycrystal model and applied to a binary aluminum-copper precipitation-hardened alloy. The alloy was heat treated at 190°C and 260°C for various times and was studied in both polycrystal and single crystal forms. Single crystals eliminated the complicating effects of grain boundaries allowing clear determination of the active deformation mechanisms, as well as a detailed study of the effect of precipitates on the flow anisotropy behavior. Different deformation mechanisms were observed corresponding to the degree of coherency between the precipitate and the matrix. The influence of precipitate-induced anisotropy on single crystal flow behavior was clearly established, again relating to the precipitate character and included in the hardening description. The physically-based hardening formulation was comprised of both statistical and geometrical storage components. Model results were compared to single crystal and polycrystal compression experiments. Accurate simulations were obtained for most of the aging conditions and the correct trends due to precipitate-induced anisotropy were predicted.

Original languageEnglish (US)
Pages (from-to)239-246
Number of pages8
JournalJournal De Physique. IV : JP
StatePublished - Mar 2003
Event6th European Mechanics of Materials Conference on Non-Linear Mechanics of Anisotropic Materials EUROMECH-MECAMAT'2002 - Liege, Belgium
Duration: Sep 9 2002Sep 12 2002

ASJC Scopus subject areas

  • Physics and Astronomy(all)


Dive into the research topics of 'Precipitate induced anisotropy effects in aluminium alloys'. Together they form a unique fingerprint.

Cite this