Micromechanical Modeling of Hydrogen Transport - A Review

Research output: Contribution to journalReview article

Abstract

Reviewing the mechanical aspects of stress corrosion cracking and hydrogen embrittlement almost 25 years ago, Rice [1, 2] indicated that an accurate analysis of hydrogen transport as affected by local stresses and strains is of primary importance toward understanding the conditions under which the mechanisms causing hydrogen embrittlement operate [3]. In 1980, Hirth in a review article [4] made it clear that trapping of hydrogen is a very important part of hydrogen embrittlement, and its significance lies behind the embrittling mechanisms. The purpose of this study is to review the models of hydrogen transport in non-hydride forming systems, and draw conclusions as regards to the hydrogen degradation effect. It should be pointed out that this review does not aim at identifying and quoting the entire literature on the subject, which is voluminous. In fact, there is a number of recent articles devoted on various specific issues of hydrogen transport, and related issues of trapping [5-12]. Rather, the effort will be directed toward providing the status of our current understanding of hydrogen transport, and in particular how solid mechanics methodology can help in this direction.

Original languageEnglish (US)
Pages (from-to)70-103
Number of pages34
JournalASTM Special Technical Publication
Issue number1401
StatePublished - Jan 1 2001

Fingerprint

Hydrogen
Hydrogen embrittlement
Stress corrosion cracking
Mechanics
Degradation

Keywords

  • Diffusion
  • Embrittlement
  • Fracture
  • Hydrogen
  • Plasticity
  • Transport

ASJC Scopus subject areas

  • Engineering(all)

Cite this

Micromechanical Modeling of Hydrogen Transport - A Review. / Sofronis, Petros; Taha, Ahmed.

In: ASTM Special Technical Publication, No. 1401, 01.01.2001, p. 70-103.

Research output: Contribution to journalReview article

@article{469f945a83ca4619af2159e8c37c5ed2,
title = "Micromechanical Modeling of Hydrogen Transport - A Review",
abstract = "Reviewing the mechanical aspects of stress corrosion cracking and hydrogen embrittlement almost 25 years ago, Rice [1, 2] indicated that an accurate analysis of hydrogen transport as affected by local stresses and strains is of primary importance toward understanding the conditions under which the mechanisms causing hydrogen embrittlement operate [3]. In 1980, Hirth in a review article [4] made it clear that trapping of hydrogen is a very important part of hydrogen embrittlement, and its significance lies behind the embrittling mechanisms. The purpose of this study is to review the models of hydrogen transport in non-hydride forming systems, and draw conclusions as regards to the hydrogen degradation effect. It should be pointed out that this review does not aim at identifying and quoting the entire literature on the subject, which is voluminous. In fact, there is a number of recent articles devoted on various specific issues of hydrogen transport, and related issues of trapping [5-12]. Rather, the effort will be directed toward providing the status of our current understanding of hydrogen transport, and in particular how solid mechanics methodology can help in this direction.",
keywords = "Diffusion, Embrittlement, Fracture, Hydrogen, Plasticity, Transport",
author = "Petros Sofronis and Ahmed Taha",
year = "2001",
month = "1",
day = "1",
language = "English (US)",
pages = "70--103",
journal = "ASTM Special Technical Publication",
issn = "0066-0558",
number = "1401",

}

TY - JOUR

T1 - Micromechanical Modeling of Hydrogen Transport - A Review

AU - Sofronis, Petros

AU - Taha, Ahmed

PY - 2001/1/1

Y1 - 2001/1/1

N2 - Reviewing the mechanical aspects of stress corrosion cracking and hydrogen embrittlement almost 25 years ago, Rice [1, 2] indicated that an accurate analysis of hydrogen transport as affected by local stresses and strains is of primary importance toward understanding the conditions under which the mechanisms causing hydrogen embrittlement operate [3]. In 1980, Hirth in a review article [4] made it clear that trapping of hydrogen is a very important part of hydrogen embrittlement, and its significance lies behind the embrittling mechanisms. The purpose of this study is to review the models of hydrogen transport in non-hydride forming systems, and draw conclusions as regards to the hydrogen degradation effect. It should be pointed out that this review does not aim at identifying and quoting the entire literature on the subject, which is voluminous. In fact, there is a number of recent articles devoted on various specific issues of hydrogen transport, and related issues of trapping [5-12]. Rather, the effort will be directed toward providing the status of our current understanding of hydrogen transport, and in particular how solid mechanics methodology can help in this direction.

AB - Reviewing the mechanical aspects of stress corrosion cracking and hydrogen embrittlement almost 25 years ago, Rice [1, 2] indicated that an accurate analysis of hydrogen transport as affected by local stresses and strains is of primary importance toward understanding the conditions under which the mechanisms causing hydrogen embrittlement operate [3]. In 1980, Hirth in a review article [4] made it clear that trapping of hydrogen is a very important part of hydrogen embrittlement, and its significance lies behind the embrittling mechanisms. The purpose of this study is to review the models of hydrogen transport in non-hydride forming systems, and draw conclusions as regards to the hydrogen degradation effect. It should be pointed out that this review does not aim at identifying and quoting the entire literature on the subject, which is voluminous. In fact, there is a number of recent articles devoted on various specific issues of hydrogen transport, and related issues of trapping [5-12]. Rather, the effort will be directed toward providing the status of our current understanding of hydrogen transport, and in particular how solid mechanics methodology can help in this direction.

KW - Diffusion

KW - Embrittlement

KW - Fracture

KW - Hydrogen

KW - Plasticity

KW - Transport

UR - http://www.scopus.com/inward/record.url?scp=1942446237&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=1942446237&partnerID=8YFLogxK

M3 - Review article

AN - SCOPUS:1942446237

SP - 70

EP - 103

JO - ASTM Special Technical Publication

JF - ASTM Special Technical Publication

SN - 0066-0558

IS - 1401

ER -