InxGa1-xas nanowires on silicon: One-dimensional heterogeneous epitaxy, bandgap engineering, and photovoltaics

Jae Cheol Shin, Kyou Hyun Kim, Ki Jun Yu, Hefei Hu, Leijun Yin, Cun Zheng Ning, John A. Rogers, Jian Min Zuo, Xiuling Li

Research output: Contribution to journalArticle

Abstract

We report on the one-dimensional (1D) heteroepitaxial growth of In xGa1-xAs (x = 0.2-1) nanowires (NWs) on silicon (Si) substrates over almost the entire composition range using metalorganic chemical vapor deposition (MOCVD) without catalysts or masks. The epitaxial growth takes place spontaneously producing uniform, nontapered, high aspect ratio NW arrays with a density exceeding 1 ×108/cm2. NW diameter (∼30-250 nm) is inversely proportional to the lattice mismatch between InxGa1-xAs and Si (∼4-11%), and can be further tuned by MOCVD growth condition. Remarkably, no dislocations have been found in all composition InxGa1-xAs NWs, even though massive stacking faults and twin planes are present. Indium rich NWs show more zinc-blende and Ga-rich NWs exhibit dominantly wurtzite polytype, as confirmed by scanning transmission electron microscopy (STEM) and photoluminescence spectra. Solar cells fabricated using an n-type In0.3Ga0.7As NW array on a p-type Si(111) substrate with a ∼2.2% area coverage, operates at an open circuit voltage, Voc, and a short circuit current density, J sc, of 0.37 V and 12.9 mA/cm2, respectively. This work represents the first systematic report on direct 1D heteroepitaxy of ternary InxGa1-xAs NWs on silicon substrate in a wide composition/bandgap range that can be used for wafer-scale monolithic heterogeneous integration for high performance photovoltaics.

Original languageEnglish (US)
Pages (from-to)4831-4838
Number of pages8
JournalNano letters
Volume11
Issue number11
DOIs
StatePublished - Nov 9 2011

ASJC Scopus subject areas

  • Bioengineering
  • Chemistry(all)
  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'In<sub>x</sub>Ga<sub>1-x</sub>as nanowires on silicon: One-dimensional heterogeneous epitaxy, bandgap engineering, and photovoltaics'. Together they form a unique fingerprint.

  • Cite this