Incipient slip and long range plastic strain localization in microtextured Ti-6Al-4V titanium

High resolution scanning electron microscope digital image correlation (SEM DIC) was performed in situ during uniaxial loading on Ti-6Al-4V rolled titanium plate to determine the dependence of strain localization on microstructure and microtexture. Individual grains with preferred orientation for basal slip exhibited plastic localization along basal planes before macroscopic yielding. With additional strain, but still below macroscopic yielding, pyramidal and prismatic plastic activity was observed as slip bands transmitting across many grains and entire microtextured regions (MTRs). The localization of long range plastic strain occurred within MTRs that allowed for slip transmission across grains with low angle boundaries. The rolled titanium plate material having strong [0001][101 0]texture components showed pyramidal and prismatic type slip extending across entire MTRs at strains well below macroscopic yielding. These strain localization processes occur much earlier in straining and over lengthscales much longer than observed with conventional slip offset imaging. The implications for properties are discussed.