Abstract

We report in situ measurements of irradiation-induced creep on amorphous (a-) Cu56Ti38Ag6, Zr52Ni48, Si, and SiO2. Micropillars 1 μm in diameter and 2 μm in height were irradiated with ∼2 MeV heavy ions during uniaxial compression at room temperature. The creep measurements were performed using a custom mechanical testing apparatus utilizing a nanopositioner, a silicon beam transducer, and an interferometric laser displacement sensor. We observed Newtonian flow in all tested materials. For a-Cu56Ti38Ag6, a-Zr52Ni48, a-Si, and Kr+ irradiated a-SiO2 irradiation-induced fluidities were found to be nearly the same, ≈3 GPa-1 dpa-1, whereas for Ne+ irradiated a-SiO2 the fluidity was much higher, 83 GPa-1 dpa-1. A fluidity of 3 GPa-1 dpa-1 can be explained by point-defect mediated plastic flow induced by nuclear collisions. The fluidity of a-SiO2 can also be explained by this model when nuclear stopping dominates the energy loss, but when the electronic stopping exceeds 1 keV/nm, stress relaxation in thermal spikes also contributes to the fluidity.

Original languageEnglish (US)
Article number024310
JournalJournal of Applied Physics
Volume117
Issue number2
DOIs
StatePublished - Jan 14 2015

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Direct measurements of irradiation-induced creep in micropillars of amorphous Cu<sub>56</sub>Ti<sub>38</sub>Ag<sub>6</sub>, Zr<sub>52</sub>Ni<sub>48</sub>, Si, and SiO<sub>2</sub>'. Together they form a unique fingerprint.

  • Cite this