Assessment of the mechanical performance of thick composite laminates manufactured by continuous curing

Keyphrases

• Mechanical Performance 100%
• Thick Composite Laminate 100%
• Optical Microscopy 50%
• Graphite-epoxy Composite 50%
• Manufacturing Cycle 50%
• Mechanical Testing 50%
• Image Analysis 50%
• Thermal Distribution 50%
• Optical Image 50%
• Material Degradation 50%
• Manufacturing Methods 50%
• Thick Composites 50%
• New Composite Materials 50%
• Composite Manufacturing 50%
• Curing Process 50%
• Void Volume 50%
• Destructive Testing 50%
• Interlaminar Shear Strength 50%
• Transverse Strength 50%
• Longitudinal Compressive Forces 50%
• Fibre Volume Distribution 50%
• Microscopic Analysis 50%
• Laminate Thickness 50%
• DSC Test 50%

Material Science

• Mechanical Strength 100%
• Differential Scanning Calorimetry 100%
• Mechanical Testing 100%
• Ultimate Tensile Strength 100%
• Materials Degradation 100%
• Shear Strength 100%
• Composite Laminate 100%
• Compressive Strength 100%

Engineering

• Mechanical Performance 100%
• Image Analysis 50%
• Ultimate Tensile Strength 50%
• Test Specimen 50%
• Materials Degradation 50%
• Manufacturing Technique 50%
• Interlaminar Shear Strength 50%
• Laminate Thickness 50%
• Destructive Testing 50%
• Compressive Strength 50%